Postalloy® DuraMang™ 2865-FCO
Postalloy® DuraMang™ 2865-FCO is a flux-cored, open-arc hardfacing wire that deposits fully austenitic chromium-manganese weld metal. It can be used equally well for joining and build-up/surfacing of carbon, low alloy and manganese steels. Weld deposits have an excellent combination of weld metal strength, ductility and hardness. Work-hardens rapidly under repeated impact. Deposits have very good frictional wear properties and are ideal for railroad applications requiring metal-to-metal wear resistance. Ideal as a cushioning or buffer layer on manganese steel parts that will be repeatedly rebuilt. Since it will not embrittle until 1000°F (538°C), it will act as an insulator to the manganese base metal in helping it keep below 500°F (260°C) during the welding operation.
Specifications
Product Type
- Wire
- Flux-cored
- Open-arc
Applications
- Pulverizing hammers
- Gyratory crusher mantles
- Dragline and power shovel bucket lips and teeth
- Crusher rolls and jaws
- Sizing screens
- Cone and roll shells
- Grizzly bars
- Hammer mill hammers
- Steel mill wobblers
Weld Deposit Properties
- Tensile Strength:
- 122,000 psi
- Yield Strength:
- 80,000 psi
- Elongation:
- 40%
- Hardness as deposited:
- 20Rc
- Work hardens in service to:
- 45-55Rc
- Deposits cannot be flame cut
- Machinable:
- Poor
Welding Parameters
Current Type: DC Electrode Positive
| Volts | Amps | Diameter | Stick Out |
|---|---|---|---|
| 24-28 | 100-175 | .045" (1.1mm) | 1"(25mm) |
| 26-29 | 150-20 | 1/16" (1.6mm) | 1"-1¼"(25-32mm) |
| 24-28 | 300-450 | 7/64" (2.8mm) | 1¼"-1½"(32-38mm) |
Welding Procedure:
Product Equivalent:
Electrode: Postalloy® 207
Packaging Options
| Diameter | Standard Packaging | Standard Packaging Available |
|---|---|---|
| .045" (1.1mm) | 25 lb (11.30kg) spool | 220 lb (99.8kg) drum |
| 1/16" (1.6mm) | 25 lb (11.30kg) spool | 220 lb (99.8kg) drum |
| 7/64" (2.8mm) | 55 lb (25kg) coil |